| HIPS 4241 法国阿托菲纳公司 物性数据 |
| 暂无此原料描述部分┄ |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | --- | ASTM D-1238 | 4 | g/10min |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.04 | g/cm3 |
| 机械性能 | 揉曲模量 | --- | ASTM D-790 | 20000 | kg/cm2 |
| 洛氏硬度 | --- | ASTM D-785 | R-76 | --- | |
| IZOD冲击强度 | --- | ASTM D-256 | 10 | kg.cm/cm | |
| 拉伸屈服强度 | --- | ASTM D-638 | 260 | kg/cm2 | |
| 断裂伸长率 | --- | ASTM D-638 | 55 | % | |
| 挠曲强度 | --- | ASTM D-790 | 45 | kg/cm2 | |
| 加工性能 | 模收缩率 | --- | ASTM D-955 | 0.4-0.7 | % |
| 加工溶融温度 | --- | --- | 200-240 | ℃ | |
| 热 性 能 | 干燥温度 | --- | --- | 70 | ℃ |
| 可燃性 | --- | UL-94 | HB | --- | |
| 热变形温度 | --- | ASTM D-648 | 73 | ℃ | |
| 维卡软化点 | --- | ASTM D-1525 | 97 | ℃ | |
| 维卡软化点 | 5kg | ASTM D-1525 | 89 | ℃ | |