| 牌号 | 6140 |
| 厂家(产地) | 美国杜邦 |
| 阻燃等级 | 0 |
阻燃LCP 6140美国杜邦物性数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 比重 | ASTM D-792 | 1.77 | ||
| IZOD冲击强度 | 3.2mm | ASTM D-256 | 85 | J/m |
| 断裂伸长率 | 3.2mm | ASTM D-638 | 1.4 | % |
| 弯曲强度 | 3.2mm | ASTM D-790 | 177 | MPa |
| 拉伸强度 | 3.2mm | ASTM D-638 | 132 | MPa |
| 弯曲模量 | 3.2mm | ASTM D-790 | 15200 | MPa |
| 模压温度范围 | 30-95 | ℃ | ||
| RTI Mechanical with Impact | 3.0mm | UL 746-B | 220 | ℃ |
| RTI Mechanical with Impact | 3.0mm | UL 746-B | 240 | ℃ |
| RTI Mechanical with Impact | 1.0mm | UL 746-B | 240 | ℃ |
| 化转变温度 | ASTM D-3418 | 120 | ℃ | |
| RTI Electrical | 3.0mm | UL 746-B | 240 | ℃ |
| RTI Mechanical with Impact | 1.0mm | UL 746-B | 210 | ℃ |
| 干燥温度 | 135 | ℃ | ||
| 熔点 | ASTM D-3418 | 335 | ℃ | |
| RTI Electrical | 1.0mm | UL 746-B | 240 | ℃ |
| 热变形温度 | 1.80MPa | ASTM D-648 | 272 | ℃ |
| 解链温度范围 | 350-360 | ℃ | ||
| Rating@Thickness | UL 746-B | V-0 | ||
| Thickness Tested | UL 94 | 1.5 | mm |