| 牌号 | G-2530 |
| 厂家(产地) | 日本出光 |
| 规格级别 | 注塑 |
聚碳酸酯PC G-2530日本出光技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | 23℃水中24h | ASTM D-570 | 0.11 | % |
| 比重 | ASTM D-792 | 1.42 | ||
| 螺线流动长度 | 3mm厚 | 出光法 | 23 | cm |
| 引张弹性率 | ISO R-527 (ASTM D-638) | 8100(83000) | MPa(KG/cm2) | |
| 挠曲弹性率 | ISO 178 (ASTM D-790) | 8530(8700) | MPa(KG/cm2) | |
| 引张破坏伸率 | ISO R-527 (TM D-638) | 3 | % | |
| IZOD冲击强度 | 4mm with notch 3.2mm with notch | ISO 180 (ASTM D-256) | 15(16) | KJ/m2(kgfcm/cm2) |
| 洛氏硬度 | ISO 2039-2 (ASTM D-785) | M92 | ||
| 引张破坏强度 | ISO R-527 (ASTM D-638) | 120(1200) | MPa(KG/cm2) | |
| 挠曲强度 | ISO 178 (ASTM D-790) | 170(1700) | MPa | |
| 诱电正接 | 60Hz | ASTM D-150 | 8×10-4 | |
| 诱电正接 | 106Hz | ASTM D-150 | 9×10-3 | |
| 体积固有抵抗 | ASTM D-257 | ＜1010 | Ω?cm | |
| 诱电率 | 106Hz | ASTM D-150 | 3.45 | |
| 绝缘破坏电压 | 1.6mm厚 | ASTM D-149 | ＜22 | kv/mm |
| 诱电率 | 60Hz | ASTM D-150 | 3.40 | |
| 耐电弧性 | ASTM D-495 | 110 | Sec | |
| 成型收缩率(MD) | ASTM D-955 | 1.5 | ||
| 成型收缩率(TD) | ASTM D-955 | 6.0 | ||
| 维卡软化点 | ISO 306 | 150 | ℃ | |
| 线膨胀系数 | ASTM D-696 | 2.3 | ×10-5cm/cm/℃ | |
| 燃烧性 | 1.47mm厚 | UL 94 | V-2 | |
| 负荷挠曲温度 | 1.80MPa 18.6kg/cm2 | ISO 75(ASTM D-648) | 144 | ℃ |