| 牌号 | GH |
| 厂家(产地) | 日本可乐丽 |
| 密度 | 1.19 g/cm3 |
| 拉伸强度 | 70 MPa |
| 成型收缩率 | 0.004 % |
| 缺口冲击强度 | 1.5 |
| 吸水率 | 0.3 % |
PMMA GH日本可乐丽物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | ASTM D-570 | 0.3 | % | |
| 全光线透过率 | ASTM D-1003 | 93 | % | |
| 比重 | ASTM D-792 | 1.19 | ||
| 阻燃性 | 1.6mm | UL 94 | HB | |
| 弯曲弹性率 | ASTM D-790 | 3.3×104 | kgf/cm2 | |
| 抗拉强度 | ASTM D-638 | 720 | kgf/cm2 | |
| 弯曲强度 | ASTM D-790 | 1050 | kgf/cm2 | |
| 洛氏硬度 | ASTM D-785 | 101 | M标度 | |
| IZOD冲击强度 | ASTM D-256 | 1.5 | kg.cm/cm | |
| 伸长率 | ASTM D-638 | 5 | % | |
| 损耗因数 | 103Hz | ASTM D-150 | 0.04 | |
| 介电强度 | ASTM D-149 | 20 | KV/mm | |
| 介电常数 | 103Hz | ASTM D-150 | 3 | |
| 体积电阻系数 | ASTM D-257 | ＜1015 | Ω.cm | |
| 成形收缩率 | ASTM D-955 | 0.002～0.006 | cm/cm | |
| 线膨胀系数 | ASTM D-696 | 6×105 | cm/cm?℃ | |
| 热变形温度 | ASTM D-648 | 92 | ℃ | |
| 比热容 | 0.35 | cal/g?℃ |