| 牌号 | FW-700M |
| 厂家(产地) | LG化学 |
聚甲醛POM FW-700M LG化学技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 吸水率 | ASTM D-570 | 0.22 | % | |
| 比重 | ASTM D-792 | 1.44 | ||
| 模缩系数 | 20-22 | cm/cm×0.0001 | ||
| Taber磨耗量 | ASTM D-1044 | 10 | mg/1000cycles | |
| 弯曲强度 | ASTM D-790 | 950 | kg/cm2 | |
| 冲击强度(无缺口) | ASTM D-256 | 70 | kg.cm/cm | |
| 冲击强度(缺口) | TM D-256 | 7.0 | kg.cm/cm | |
| 弯曲模量 | ASTM D-790 | 26000 | kg/cm2 | |
| 洛氏硬度 | ASTM D-785 | 82 | M | |
| 伸长率 | ASTM D-638 | 40 | % | |
| 砦挤系数(动) | ASTM D-1894 | 0.14 | ||
| 砦挤系数(静) | ASTM D-1894 | 0.11 | ||
| 张力 | ASTM D-638 | 650 | kg/cm2 | |
| 缩性热伸张系数 | ASTM D-696 | 10×0.000001 | mm/mm/C | |
| 抗体积性 | ASTM D-257 | 1×1014 | Ω.cm | |
| 抗表面性 | ASTM D-257 | 1×1016 | Ω | |
| 热变形温度 | 18kg/cm2 | ASTM D-648 | 110 | C |
| 热变形温度 | 4.6kg/cm2 | ASTM D-648 | 160 | C |
| 燃烧性 | HB |