| 牌号 | 7140F |
| 厂家(产地) | 台湾塑胶 |
| 规格级别 | 薄膜级 |
| 用途 | 温室膜、农业膜、医药用途 |
| 密度 | 0.934 g/cm3 |
| 熔体流动速率 | 0.7 g/10min |
| 拉伸强度 | 19 MPa |
| 弯曲模量 | 22 MPa |
| 断裂伸长率 | 600 % |
薄膜级EVA 7140F台湾塑胶物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 密度 | ASTM D-1505 | 0.934 | g/cm3 | |
| VA含量 | 14 | % | ||
| 熔体流动速率 | ASTM D-1238 | 0.7 | g/10min | |
| 拉力降伏强度 | ASTM D-638 | 70 | Kg/cm2 | |
| 弯曲模量 | ASTM D-790 | 230 | Kg/cm2 | |
| 拉力断裂强度(MD) | ASTM D-882B | 310 | Kg/cm2 | |
| 拉力断裂强度(TD) | TM D-882B | 280 | Kg/cm2 | |
| 硬度 | ASTM D-2240 | 92 | Shore A | |
| 摩擦系数 | ASTM D-1894 | 0.5 | ||
| 抗撕裂性(MD) | ASTM D-1922 | 10 | N/mm | |
| 抗撕裂性(TD) | ASTM D-1922 | 24 | N/mm | |
| 拉力断裂伸长率 | ASTM D-638 | 750 | % | |
| 硬度 | ASTM D-2240 | 40 | Shore D | |
| 断裂伸长率(MD) | ASTM D-882B | 450 | % | |
| 断裂伸长率(TD) | ASTM D-882B | 600 | % | |
| 拉力断裂强度 | ASTM D-638 | 200 | Kg/cm2 | |
| 1%伸长弹性系数(MD) | ASTM D-882B | 370 | Kg/cm2 | |
| 1%伸长弹性系数(TD) | ASTM D-882B | 420 | Kg/cm2 | |
| 拉力降伏强度(MD) | ASTM D-882B | 50 | Kg/cm2 | |
| 拉力降伏强度(TD) | ASTM D-882B | 40 | Kg/cm2 | |
| 落球冲击强度 | ASTM D-1709 | 620 | g | |
| 软化点 | ASTM D-1525 | 75 | ℃ | |
| 脆化温度 | ASTM D-746 | -70 | ℃ | |
| 熔点 | DSC | 90 | ℃ | |
| 浊度 | ASTM D-1003 | 3 | % | |
| 光泽度 | 45℃ | ASTM D-2457 | 90 | % |
| 薄膜厚度 | 30-150 |