| 牌号 | SC-1060U |
| 厂家(产地) | 三星第一毛织 |
| 规格级别 | 透明 |
| 密度 | 1.2 g/cm3 |
| 熔体流动速率 | 6 g/10min |
| 成型收缩率 | 0.5 % |
| 缺口冲击强度 | 881 |
| 吸水率 | 0.2 % |
PC SC-1060U三星第一毛织技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 比重 | ASTM D792 | 1.20 | g/cm3 | |
| 熔体流动速率 | 300℃/1.2kg | ASTM D1238 | 6.0 | g/10min |
| 成型收缩率 | 流动 | ASTM D955 | 0.50-0.70 | % |
| 吸水率 | 24hr,23℃ | TM D570 | 0.20 | % |
| 洛氏硬度 | M计秤 | ASTM D785 | 77 | |
| R计秤 | ASTM D785 | 120 | ||
| 拉伸强度 | ASTM D638 | 64.8 | MPa | |
| 伸长率 | 断裂 | ASTM D638 | 110 | % |
| 弯曲模量 | ASTM D790 | 2280 | MPa | |
| 弯曲强度 | ASTM D790 | 91.0 | MPa | |
| 悬壁梁缺口冲击强度 | 3.18mm | ASTM D256 | 881 | J/m |
| 6.35mm | ASTM D256 | 155 | J/m | |
| 热变形温度 | 0.45MPa,未退火 | ASTM D648 | 137 | ℃ |
| 1.8MPa,未退火 | ASTM D648 | 132 | ℃ | |
| 线形膨胀系数 | 流动(40到100℃) | 0.000060-0.000080 | cm/cm/℃ | |
| 介电常数 | 10MHz | ASTM D150 | 2.90 | |
| UL阻燃等级 | 2.60mm | UL94 | HB | |
| 2.80mm | UL94 | HB | ||
| 1.60mm | UL94 | V-2 | ||
| 2.00mm | UL94 | V-2 | ||
| 透射率 | 3000m | ASTM D1003 | 89.0 | % |
| 混浊 | 3000m | ASTM D1003 | 0.80 | % |