牌号 | HY-11A |
厂家(产地) | 广州恒逸 |
规格级别 | 注塑级 |
密度 | 1.2 g/cm3 |
熔体流动速率 | 27.5 g/10min |
弯曲强度 | 80 MPa |
拉伸强度 | 65 MPa |
缺口冲击强度 | 45 |
聚碳酸酯PC HY-11A广州恒逸技术数据
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
---|---|---|---|---|
熔体流动速率 | --- | ASTM D-1238 | 25-30 | g/10min |
密度 | --- | ASTM D-792 | 1.2 | g/cc |
透明率 | --- | ASTM D-1003 | 40 | % |
收缩率 | --- | ASTM D-955 | 0.0050-0.0070 | mm/mm |
弯曲强度 | --- | ASTM D-638 | 80 | MPa |
拉伸断裂强度 | --- | TM D-638 | 65 | MPa |
断裂伸长率 | --- | ASTM D-638 | 90 | % |
弯曲模量 | --- | ASTM D-790 | 2.37 | Gpa |
悬臂梁缺口冲击强度 | --- | ASTM D-256 | 45 | KJ/m2 |
热变形温度 | 0.45MPa | ASTM D-648 | 130 | ℃ |
燃烧性 | 1.5mm | UL 94 | HB | --- |