| 牌号 | HI835M |
| 厂家(产地) | LG化学 |
| 规格级别 | 注塑 通用 |
| 密度 | 1.17 g/cm3 |
| 熔体流动速率 | 3 g/10min |
| 成型收缩率 | 0.6 % |
| 缺口冲击强度 | 3.5 |
| 吸水率 | 0.4 % |
PMMA HI835M LG化学物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 水吸收性 | 24h | ASTM D-570 | 0.4 | % |
| 反射指数 | ASTM D-542 | 1.49 | ||
| 透明性 | 3.2mm | ASTM D-1003 | 92 | % |
| 比重 | ASTM D-792 | 1.17 | ||
| 弯曲模数 | ASTM D-790 | 24100 | Kg/cm2 | |
| 拉力 | ASTM D-638 | 520 | Kg/cm2 | |
| 洛氏硬度 | M-Scale | ASTM D-785 | 70 | |
| 弯曲强度 | ASTM D-790 | 955 | Kg/cm2 | |
| 冲击强度 | Izod Notched | ASTM D-256 | 3.5 | kgcm/cm2 |
| 延伸率 | ASTM D-638 | 66 | % | |
| 介电定数 | 60Hz | ASTM D-150 | 3.5 | |
| 功率系数 | 60Hz | ASTM D-150 | 0.04 | |
| 介电强度 | 4KV/S | ASTM D-149 | 15 | KV/mm |
| 抗体积系数 | ASTM D-257 | >10 | .cm | |
| 模缩系数 | ASTM D995-51 | 0.4-0.8 | % | |
| 热变形温度 | 18.6kg | ASTM D-648 | 93 | C |
| 比热 | 0.35 | cal/g/C | ||
| 绵性膨胀系数 | ASTM D-696 | 610-5 | cm/cm/C | |
| 热传导 | ASTM D-177 | 510-4 | cal/seccmC/cm | |
| 流动指数 | 230C 3.8kg | ASTM D-1238 | 3 | g/10min |
| 维卡软化点 | 1kg | ASTM D-1525 | 103 | C |
| 燃烧度 | UL94 | HB | 1/8" 1/16" |