| 牌号 | MBZ230 |
| 厂家(产地) | 三井化学 |
| 外观颜色 | 白色不透明 |
| 密度 | 1.08 g/cm3 |
| 硬度 | 90 |
| 熔体流动速率 | 30 g/10min |
| 断裂伸长率 | 25 % |
| 吸水率 | 0.11 % |
TPX/MBZ230/三井化学技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 熔融指数 | 260℃ 5kg | ASTM D-1238 | 30 | g/10min |
| 密度 | ASTM D-1505 | 1.08 | g/cm3 | |
| 熔点 | MCI方法 | 240 | ℃ | |
| 抗张强度 | ASTM D-638 | 170 | kg/cm2 | |
| 凹口Charpy耐冲击强度 | ASTM D-256 | --- | kgcm/cm2 | |
| 断裂伸长率 | ASTM D-638 | 25 | % | |
| 曲折模数 | TM D-790 | 19 000 | kg/cm2 | |
| 抗张屈服强度 | ASTM D-638 | 240 | kg/cm2 | |
| Rockwell硬度 | ASTM D-785 | R90 | ||
| 无凹口lzod耐冲击强度 | ASTM D-256 | -- | kgcm/cm2 | |
| 曲折强度 | ASTM D-790 | 390 | kg/cm2 | |
| Olsen刚性 | ASTM D-747 | --- | kg/cm2 | |
| 介电常数 | 100～1MHz | ASTM D-150 | --- | |
| 吸水率 | 24hr | ASTM D-570 | 0.11 | % |
| 介电强度 | ASTM D-149 | --- | KV/mm | |
| 体积电阻系数 | ASTM D-257 | --- | Ωcm | |
| 介电消散因子 | 23℃ 1MHz | ASTM D-150 | 0.0014 | |
| 比热 | ASTM C-351 | --- | cal/g℃ | |
| 燃烧速率 | ASTM D-635 | --- | cm/min | |
| Vicat软化点 | ASTM D-1525 | 175 | ℃ | |
| 热变形温度 | 4.6kg/cm2 | ASTM D-648 | 110 | ℃ |
| 热传导系数 | ASTM BS-847A | --- | calcm/seccm2℃ | |
| 模收缩率(机械/垂直方向) | MCI方法 | 1.7/1.4 | % | |
| 线膨胀系数 | ASTM D-696 | --- | 1/℃ | |
| 折射率 | ASTM D-542 | --- | nd | |
| 模糊度 | ASTM D-1746 | --- | % | |
| 透光率 | ASTM D-1746 | --- | % |