| 牌号 | UE633 |
| 厂家(产地) | 台湾聚合 |
| 规格级别 | 注塑级 |
| 用途 | 射出成型热融胶 |
| 密度 | 0.938 g/cm3 |
| 硬度 | 34 |
| 熔体流动速率 | 19 g/10min |
| 脆化温度 | -76 ℃ |
| 维卡软化点 | 60 ℃ |
EVA UE633台湾聚合物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 密度 | ASTM D-1505 | 0.938 | g/cm3 | |
| 铸膜成型 | ASTM D-638/D-882 | 790 | % | |
| 融化点 | ASTM D-2117 | 82 | ℃ | |
| 熔融指数 | ASTM D-1238 | 19 | g/10min | |
| 薄膜(MD) | ASTM D-638/D-882 | 138 | kg/cm2 | |
| 薄膜(TD) | ASTM D-638/D-882 | 86 | kg/cm2 | |
| 射出 | TM D-638/D-882 | 300 | % | |
| VA含量 | ASTM USIFE | 20 | % | |
| 薄膜(MD) | ASTM D-638/D-882 | 450 | % | |
| 薄膜(TD) | ASTM D-638/D-882 | 660 | % | |
| 硬度 | ASTM D-2240 | 34 | Shore D | |
| 铸膜成型 | ASTM D-638 | 127 | kg/cm2 | |
| 低温易脆性 | ASTM D-746 | <-76 | ℃/F50 | |
| VICAT 软化点 | ASTM D-1525 | 60 | ℃ | |
| 射出 | ASTM D-638/D-882 | 72 | kg/cm2 |