| 牌号 | UE630 |
| 厂家(产地) | 台湾聚合 |
| 规格级别 | 发泡级 |
| 用途 | 压缩成型(发泡)被覆挤压吹出成型。 |
| 密度 | 0.937 g/cm3 |
| 熔体流动速率 | 1.5 g/10min |
| 拉伸强度 | 16 MPa |
| 断裂伸长率 | 68 % |
| 缺口冲击强度 | 430 |
发泡级EVA UE630台湾聚合物性数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 密度 | ASTM D-1505 | 0.937 | g/cm3 | |
| 熔体流动速率 | ASTM D-1238 | 1.5 | g/10min | |
| 硬度 | ASTM D-2240 | 36 | Shore D | |
| 低温易脆性 | ASTM D-746 | ＜-76 | ℃/F50 | |
| 冲击强度 | ASTM D-1709 | 430 | G/F50 | |
| 延展性(铸膜成型) | ASTM D-638(TM D-882) | 700 | % | |
| 延展性(射出) | ASTM D-638(ASTM D-882) | 150 | % | |
| 延展性(薄膜MD) | ASTM D-638(ASTM D-882) | 310 | % | |
| 延展性(薄膜TD) | ASTM D-638(ASTM D-882) | 670 | % | |
| 降伏点抗张强度(铸膜成型) | ASTM D-638(ASTM D-882) | 170 | KG/cm2 | |
| 降伏点抗张强度(射出) | ASTM D-638(ASTM D-882) | 122 | KG/cm2 | |
| 降伏点抗张强度(薄膜MD) | ASTM D-638(ASTM D-882) | 213 | KG/cm2 | |
| 降伏点抗张强度(薄膜TD) | ASTM D-638(ASTM D-882) | 184 | KG/cm2 | |
| 熔点 | ASTM D-2117 | 89 | ℃ | |
| 维卡软化点 | ASTM D-1525 | 67 | ℃ | |
| VA含量 | USIFE | 16 | % |