| 牌号 | C3030 |
| 厂家(产地) | 日本帝人 |
| 密度 | 1.6 g/cm3 |
| 拉伸强度 | 176 MPa |
| 成型收缩率 | 0.7 % |
| 断裂伸长率 | 1.8 % |
| 缺口冲击强度 | 98 |
PET C3030日本帝人物性数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 比重 | 23℃水中24Hr | ASTM D-792 | 1.60 | |
| 成形收缩率 | 23℃水中24Hr | 0.2/1.2 | % | |
| 冲击强度(缺口) | 1/8" | ASTM D-256 | 98 | J/M |
| 冲击强度(无缺口) | 1/8" | ASTM D-256 | 490 | J/M |
| 磨擦系数 | 对钢 | ASTM D-1894 | 0.10 | |
| 表面硬度 | ASTM D-785 | M195 | ||
| 弯曲强度 | ASTM D-790 | 245 | MPa | |
| 拉伸率 | ASTM D-638 | 1.8 | % | |
| 塔伯磨耗 | CS-171kg | ASTM D-1044 | 30 | mg |
| 弯曲弹性率 | ASTM D-790 | 9.8 | GPa | |
| 拉伸强度 | ASTM D-638 | 176 | MPa | |
| 绝缘强度 | 1mmt | ASTM D-149 | 32 | KV/mm |
| 耐电弧性 | ASTM D-495 | 116 | Sec | |
| 体积电阻 | ASTM D-257 | >10E16 | Ω.cm | |
| 介电常数(60Hz) | ASTM D-150 | 4.3 | ||
| 介电常数(1KHz) | ASTM D-150 | 4.3 | ||
| 熔点 | 254 | ℃ | ||
| 耐燃性 | UL 94 | HB | ||
| 线膨胀系数 | X10-5 | ASTM D-696 | 2.5 | cm/cm |
| 热变形温度(0.45MPa) | ASTM D-648 | 245 | ℃ | |
| 热变形温度(1.82MPa) | ASTM D-648 | 242 | ℃ |