| 牌号 | C9030 |
| 厂家(产地) | 日本帝人 |
| 密度 | 1.59 g/cm3 |
| 拉伸强度 | 142 MPa |
| 成型收缩率 | 0.75 % |
| 缺口冲击强度 | 75 |
| 吸水率 | 0.08 % |
PET C9030日本帝人物性数据
| 性能 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|
| 比重 | 23℃水中24Hr | ASTM D-792 | 1.59 | |
| 成形收缩率 | 23℃水中24Hr | 0.3/1.2 | % | |
| 吸水率 | 23℃水中24Hr | ASTM D-570 | 0.08 | % |
| 冲击强度(缺口) | 1/8" | ASTM D-256 | 75 | J/M |
| 冲击强度(无缺口) | 1/8" | ASTM D-256 | 640 | J/M |
| 拉伸强度 | ASTM D-638 | 142 | MPa | |
| 弯曲强度 | ASTM D-790 | 205 | MPa | |
| 塔伯磨耗 | CS-171kg | ASTM D-1044 | 22 | mg |
| 面硬度 | ASTM D-785 | M90 | ||
| 拉伸率 | ASTM D-638 | 3.8 | % | |
| 磨擦系数 | 对钢 | ASTM D-1894 | 0.12 | |
| 弯曲弹性率 | ASTM D-790 | 8.9 | GPa | |
| 绝缘强度 | 1mmt | ASTM D-149 | 38 | KV/mm |
| 介电常数(60HZ) | ASTM D-150 | 3.8 | ||
| 介电常数(1KHZ) | ASTM D-150 | 3.8 | ||
| 耐电弧性 | ASTM D-495 | 105 | Sec | |
| 介电损耗正切值(60HZ) | ASTM D-150 | 0.043 | ||
| 介电损耗正切值(1KHZ) | ASTM D-150 | 0.022 | ||
| 体积电阻 | ASTM D-257 | >10E16 | Ω.cm | |
| 线膨胀系数 | X10-5 | ASTM D-696 | 2.5 | cm/cm |
| 熔点 | 251 | ℃ | ||
| 热变形温度(0.45MPa) | ASTM D-648 | 240 | ℃ | |
| 热变形温度(1.82MPa) | ASTM D-648 | 235 | ℃ | |
| 耐燃性 | UL 94 | HB |